Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Carousel with three slides shown at a time. Use the Previous and Next buttons to navigate three slides at a time, or the slide dot buttons at the end to jump three slides at a time. Polyester Yarn Denier

Multifunctional auxetic and honeycomb composites made of 3D woven carbon fibre preforms | Scientific Reports

Kang Yang, Juan Guan, … Robert O. Ritchie

Emanuele Maccaferri, Matteo Dalle Donne, ... Loris Giorgini

Ji-un Jang, Hyeong Cheol Park, … Seong Yun Kim

Qing-Fang Guan, Huai-Bin Yang, … Shu-Hong Yu

Alexander D. Snyder, Zachary J. Phillips, … Jason F. Patrick

AA Megahed, MM Osama, … Ayman MM Abdelhaleem

Jun Lin, Jiao Li, … Liang Chen

Jian Song, Weidong Wen, … Yang Lu

MJ Khoshgoftar, A. Barkhordari, … MJ Mirzaali

Scientific Reports volume  12, Article number: 22593 (2022 ) Cite this article

Three dimensional (3D) woven composites started to find applications in various industrial sectors, mainly in aerospace and with a potential in automotive. 3D-woven fabrics can be architected to form complex and near-net-shape preforms ready for automated composites manufacturing. The 3D-woven honeycomb fabric is designed to include additional functionality into finished composites, such as positive and negative Poisson's ratios. In this study, complex honeycomb architectures were created using various weave designs to demonstrate the effects of auxetic behaviours when manufactured into a composite structure. A Staubli 3D-weaving system equipped with Jacquard UNIVAL 100 and creel of 3072 6 k carbon fibre tows were used to weave the designed honeycomb architecture. With the aid of hard polyester foam inserts, the 3D-woven fabrics were converted to honeycomb and auxetic preforms. These preforms were infused using epoxy resin to manufacture a set of honeycomb and auxetic composite structures. In comparison with the baseline honeycomb structure, it is proven that the developed auxetic composites exhibited negative Poisson’s ratio of − 2.86 and − 0.12 in the case of tensile and compression tests respectively.

Multifunctional 3D woven composites have the ability to absorb energy through progressive failure, whilst maintaining gradual load profile decay beyond the failure onset1,2. Consequently, they are of great interest for situations where the ability to withstand crash or impact loading is a design requirement. 3D woven composites are starting to find applications in various sectors, particularly aerospace and automotive applications. Several OEMs and Tier 1 manufacturers are actively investigating these structures. In aerospace, 3D woven structures are already used in fan blades and fan casings. Development is at an early stage and there are many opportunities for improving impact performance and optimising the weight of the structure. It is important that crash structures used in vehicles like cars, buses and trains are accurately predictable and the manufacturing is repeatable. There is also an opportunity using 3D weaving to add an additional functionality into composites.

3D weaving is a specialist activity and there are very few centres capable of conducting the research needed. Textile manufacturers such as DORNIER and STAUBLI manufacture 3D weaving machines but 3D woven fabrics for composites applications are currently in their infancy. In the UK, companies such as Sigmatex UK Ltd, M Wrights & Sons and Antich & Sons have developed internal capabilities to utilise 3D weaving, but more R&D is required to deploy such technology throughout the supply chain. Recently the University of Sheffield AMRC established 3D weaving capabilities which will be used to bridge the gap and support industry.

3D woven preforms have the capability to demonstrate multifunctionality in the manufacture of advanced composites. One of the 3D multifunctional structures is the auxetic functionality which needs to be investigated and demonstrated to industry. This could be in the form of expandable honeycomb type structures3, which could be woven and tested to show capability and potentially improved mechanical performances with high damage tolerance such as crash, compression and impact. Figure 1 explains what the auxetic structure is compared to the conventional honeycomb structure in terms of its geometry, i.e., an auxetic material exposed to tension would increase in dimensions in the direction that is lateral to an applied tensile force. An auxetic structure has several advantages in a crash situation for example good energy absorption, however, the repeatable manufacture of an auxetic structure with a predictable behavior needs further work4.

Conventional honeycomb (a) and auxetic (b) structures under tension.

Poisson’s ratio, which is the ratio of the strain normal to the applied load to the extension strain (or axial strain) in the direction of the applied load. Poisson's ratio (\(\nu\) ) of standard material can be expressed as:

where, εt = transverse strain, εl = longitudinal or axial strain, ∆L = change in length, Lo = initial length, ∆T = change in width and To = initial width.

Most conventional materials show positive Poisson's ratio (PPR) under tensile loads because they exhibit positive longitudinal and negative transverse strains, but smart materials like auxetics behave oppositely and show negative Poisson's ratio (NPR).

It is known that conventional materials such as rubber and metals laterally contract when stretched and laterally expand when compressed in the longitudinal direction; such materials have a PPR. In contrast, there are some special materials which possess a NPR which laterally expand when stretched or laterally shrink when compressed in the longitudinal direction. The materials with NPR are also called ‘auxetics’, which originated from the Greek word ‘auxetos’ meaning ‘that which may be increased’5. Auxetics could be materials and/or structures, they have been investigated in the literature from different perspectives such as developing materials and structures, comparing behaviours and testing performances.

In comparison with conventional materials, auxetic structures have many improved properties. They have higher shear modulus, hence better shear resistance. Auxetic materials have enhanced indentation/impact resistance and energy absorbance properties. When conventional material is subjected to an impact force, the material moves away from the impact point, but exhibiting the opposite behaviour, the auxetic material flows towards to impact point, which makes the auxetic materials harder to be indented. They also have other advantages, such as enhanced fracture toughness, improved crack growth resistance and higher damping resistance. Due to these advantages, auxetic composite structures could find suitable applications in high value manufacturing, such as aerospace and automotive sectors. The disadvantage of auxetic composites is that they may be difficult to manufacture on a large scale 5, but such difficulty has been challenged in this work.

Many studies have been conducted to develop and investigate new auxetic structures and materials based on different material scales. The examples include auxetic fibers6,7, auxetic fabrics8,9, auxetic foams10,11, and auxetic composites12,13. Auxetic woven-composite structures are investigated in this project. Zhou et al.14 developed auxetic composites made of 3D orthogonal woven textile and polyurethane foam. They prove that the auxetic composites exhibited NPR and behave more like damping material with lower compression stress, while the non-auxetic composites behaves more like stiffer material with higher compression stress. In another study15 3D-woven structures were produced and the effect of float length of ground weave and binding yarn on auxeticity of the fabric was investigated. A set of different 3D orthogonal woven structures were produced on a rapier dobby loom by changing the float length in the ground weave and binding yarns. The results showed that the 3D-woven materials with equal and maximum float length of ground weave and binding yarn showed greater auxetic behavior. Also, the impact energy absorption of the developed composites was found to increase with the increase in float length, justifying that the structures are auxetic and possess NPR. Zulifqar and Hu16 reported that the woven fabric could be auxetic through a combination of loose weave and tight weave in the same structure. They showed that the developed fabrics exhibit NPR effect in both weft and warp directions in a large range of tensile strain.

In this work, a Staubli 3D Weaving System was utilised, including Unival jacquard to weave 3D honeycomb fabrics using Toray T300-6 k carbon fibres fed from warp and weft directions. With the aid of polyester foam, the developed 3D-woven fabrics were converted to two different preforms: conventional honeycomb and new auxetic structures. The preforms were infused using epoxy resin to manufacture large composite structures investigated in this study. Tensile and compression tests were carried out to assess the functionality of honeycomb and auxetic composite structures through their Poisson’s ratio measurements.

Carbon fibre (CF), thermoset resin system and hard PET foam were used to preform and manufacture composite structures. Their grade and properties are given Table 1:

According to the resin manufacturer, the T-Prime 130–1 was mixed at 100/27 by wt% of resin/hardener to infuse the dry preforms.

EAT weave-design software was used to design a complex honeycomb structure. A schematic diagram of the honeycomb design suggested in this study is shown in Fig. 2. The unit cell of this honeycomb structure (Fig. 2) consists of a number of plain weaves of different number of layers; single-layer weave (A), two-layer weave (B, C), four-layer weave (D), and three-layer weave (E).

Honeycomb structure, (A,B,C,D,E) are plain weaves of different number of layers; 1-layer (A), 2-layer (B, C), 4-layer (D) and 3-layer (E).

Using the EAT software, a colour coding system has been firstly allocated and then assigned to the different weave designs selected to form the suggested honeycomb structure. Table 2 below presents the number of picks and pick density of the different zones defined within the structure designed. Figure 3 shows the EAT assigned weaves (red, yellow and green zones) include JC5 file of the honeycomb design installed for the Jacquard UNIVAL 100.

Weave designs used for the repeat zones (Red, Yellow and Green) given in Table 2 using JC5 output file from EAT software.

The main goal of this research is to demonstrate a 3D woven composite structure that can exhibit a smart functionality such as an auxetic structure of NPR. The honeycomb structure designed in this study (Fig. 2) is converted to the auxetic one as shown in Fig. 4.

The 3D weaving system (creel, Jacquard, loom and horizontal take off table) was used to produce the honeycomb fabric. The 3D weaving system (Fig. 5) was threaded with 3072 carbon fibre tows through the warp direction and the same fibre was also used through the weft direction. 16 ends per dent was drawn in through the reed. 128 ends (64 from each side) of the 3072 ones were loaded with polyester (PET) yarn and used as selvage catch cord to lock both edges of the woven fabric (Fig. 6).

A schematic of the 3D weaving system.

The 3D weaving machine in operation with fibres loaded at the back (left) and fabric produced at the front (right) of the loom.

According to Table 2, samples of 3D-woven fabrics of three different pick densities (6, 8 and 10 pick/cm) were manufactured. Figure 7 demonstrates a selection of photos of the honeycomb fabric produced, blank samples on the left and open cross-sections on the right.

Samples of 3D woven honeycomb fabric.

In order to minimise errors, trials and to save materials, a soft foam insert/core was used to preform the woven fabric into the honeycomb and auxetic structures prior to resin infusion. The dry fibre preform structure was made to test its formability and functionality in particular the auxetic one. The foam was cut to the relevant shapes and was inserted into the fabric pockets. The honeycomb structure (Fig. 8a) achieved its targeted preform shape relatively easily, but the auxetic preform (Fig. 8b) needed some additional supports (in the form of G-clamps) in order to hold the shape.

Dry fibre honeycomb (a) and auxetic (b) preforms. Length and height measurements at the start (c) and the end (d) of the manual testing of auxetic preform.

As a dry preform, the functionality of the auxetic structure was tested to confirm its negative Poisson’s ratio. Snapshots (Fig. 8c and Fig. 8d) were captured during the manual tensile testing. The longitudinal and transverse parameters such as the initial length (Lo) and height (To) were measured and highlighted on Fig. 8c,d. The units of measurements are ignored here as the strain is dimensionless and such measurements were taken online using a virtual ruler. The longitudinal and transverse strains and then Poisson’s ratio were calculated and listed in Table 3. The Poisson’s ratio is found to be negative (− 0.78) which confirms that the preform is showing auxetic behaviour.

Due to the high complexity of the woven structures, the resin infusion and vacuum bagging method was employed in this study. To avoid squashing and compressing the soft foam, used above in Fig. 8 during the vacuuming process, alternative hard and high-density PET foam (Divinycell P150) was used to preform the honeycomb structure prior to infusion. The foam inserts were wrapped with release film to ease demoulding after curing. Figure 9a,b,c shows an example of bagging process of honeycomb preforms including the resin infusion of both honeycomb and auxetic structures. An infusion mesh or a resin flow assist material (blue) was used to encourage flow in particular across the preform as shown in Fig. 9.

Bagging process of honeycomb preform (a) and resin infusion of honeycomb (b) and auxetic (c) assembles.

Gurit T-Prime 130–1 resin and hardener were used to infuse the woven preforms produced in this research. The mixing ratio of resin to hardener used in these infusions was 100:27 by weight, as prescribed by the manufacturer’s TDS. Table 4 gives the mixing ratio used in grams. After degassing the mixture for 10 min, the infusion took place and was completed in around 30 min. Subsequently, the assembly was moved to a preheated oven and cured at 60 °C for 3 h. Figure 10 demonstrates a selection of the manufactured honeycomb and auxetic composite structures.

Cured honeycomb (top) and auxetic (bottom) composite structures.

Mechanical tests were carried out to determine the Poisson’s ratio for the honeycomb and auxetic composite structures manufactured in this study. Despite the conventional samples such as flat and cylindrical coupons, there are no standard methods available to determine Poisson’s ratio of such complicated structures developed in this research. Instron testing machines were used to have a good control and determine the force–displacement graphs precisely. The two composite structures are subjected to tensile and compression tests, the results of which are detailed in the following sections.

Prior to testing, the length and height of the auxetic and honeycomb samples were measured as shown and given in Fig. 11. A transducer was used to ensure precise and online measurement of the transverse displacement during the test. The test repeats were recorded and two screenshots were captured to determine the initial and final transverse displacements. In the case of the auxetic structure, Fig. 12 shows the start (left) and end (right) positions of the tensile test.

Tensile test setup of auxetic (left) and honeycomb (right) structures.

The start (left) and end (right) positions of tensile test for the auxetic structure.

Figure 13a,b shows the maximum longitudinal (L) and transverse (T) displacements of the auxetic structure recorded during the test. Due to the complexity and rigidity of the tested structure, it is noticed that the transducer has been slightly deviated from the original position at the start of the test (Fig. 13). To overcome this misalignment, the measurements of the transverse displacement were also recoded from the grid background (graph paper). From the measurements made and the figures above, Table 5 listed the measurements obtained. It is found that the Poisson’s ratio of the tested structure is − 2.86, i.e. the auxetic composite exhibited NPR in the case of the tensile testing.

Longitudinal (a) and transverse (b) displacements recorded in the case of tensile test of auxetic structure.

In the case of the honeycomb structure, Fig. 14 shows the start and end positions of the tensile test. The longitudinal and transverse displacements of honeycomb structure recorded during the tensile test are shown in Fig. 15a,b and the Poisson’s ratio results are given in Table 6. It is found that the Poisson’s ratio of the tested structure is 8.10, i.e. as expected the honeycomb composite exhibited PPR in the case of the tensile testing.

The start (left) and end (right) positions of tensile test for the honeycomb structure.

Longitudinal (a) and transverse (b) displacements of the honeycomb structure recorded during the test.

In the case of compression test setup, a ruler was used as an indicator of the transverse displacement instead of the transducer used in the tensile test. Different symbols were used in this test due to the change of the load direction. For the auxetic sample, the original length is noted do which measured 710 mm whilst the original height ho measured 170 mm. The dimensions of do and ho for the honeycomb were 787 mm and 160 mm respectively. As shown in Fig. 16, a small section was highlighted on the ruler to measure the displacement in the longitudinal direction. Figure 16 shows the start and end positions of the compression test for the auxetic structure. Table 7 gives the measured displacements, strains and Poisson’s ratio of auxetic composite. It is found that the Poisson’s ratio of the tested auxetic structure is − 0.12, i.e. the auxetic composite also exhibited NPR in the case of the compression testing. It is proven that the auxetic composite structure revealed NPR under tensile and compression loads.

The start (left) and end (right) positions of compression test for the auxetic structure.

In terms of the honeycomb structure, Fig. 17 shows the start and end positions of compression test. Table 8 gives the measured displacements, strains and Poisson’s ratio of honeycomb composite. It is found that the Poisson’s ratio of the tested honeycomb structure is 0.11, i.e. the honeycomb composite also exhibited PPR in the case of the compression testing.

The start (left) and end (right) positions of compression test for the honeycomb structure.

In summary, it is found that the auxetic composite structure exhibited NPP (− 2.86 & − 0.12), whereas the honeycomb structure showed PPR (8.10 & 0.11) under both testing mechanisms (tensile and compression). But in the case of the tensile test, the Poisson’s ratio obtained for both structures are found to be out of the normal range of standard materials (− 1 to 1) which may be due to the specific structures developed in this work.

3D honeycomb structures were successfully woven and the use of a supportive core material (in this case foam) was needed to allow the dry 3D woven fabrics to be preformed and resin infused. As a dry fibre, the auxetic preform was manually tested and its auxetic functionality was successfully proven. Dry preforms (honeycomb and auxetic) were infused using epoxy resin then the cured honeycomb and auxetic composites were successfully tested using tensile and compression tests. The honeycomb structure exhibited positive Poisson’s ratios (PPR) in both testing directions (tensile and compression), but the auxetic structure demonstrated a negative Poisson’s ratio (NPR) and thereby exhibited smart functionality. The concept of 3D woven smart functionality composites is proven, and multifunctional 3D woven composites are demonstrated. The values of Poisson’s ratio obtained for both structures are found to be outside the range of conventional materials in the case of the tensile test.

Future work is recommended to manufacture generic panels or demonstrators made of honeycomb/auxetic composites and investigate their mechanical performance through different responses such as impact and crash tests. Furthermore, the very high Poisson’s ratio for the honeycomb structure will be explored further to see if this can be exploited in new applications.

The raw data of tests carried out in this study is available upon request and here it is a link for it.

Castaneda, N., Wisner, B., Cuadra, J., Amini, S. & Kontsosa, A. Investigation of the Z-binder role in progressive damage of 3D woven composites. Compos. Part A Appl. Sci. Manuf. 98, 149 (2017).

Yan, S., Zeng, X. & Long, A. Experimental assessment of the mechanical behaviour of 3D woven composite T-joints. Compos. Part B Eng. 154, 108–113 (2018).

Geerinck, R. et al. One-shot production of large-scale 3D woven fabrics with integrated prismatic shaped cavities and their applications. Mater. Des. 165, 107578 (2019).

Evans, K. E., Nkansah, M. A., Hutchinson, I. J. & Rogers, S. C. Molecular network design [7]. Nature 353, 124–124 (1991).

Article  ADS  CAS  Google Scholar 

Wang, Z., Zulifqar, A. & Hu, H. Auxetic composites in aerospace engineering. In Advanced Composite Materials for Aerospace Engineering (eds Rana, S. & Fangueiro, R.) 213–240 (Elsevier, Amsterdam, 2016).

Ravirala, N., Alderson, K. L., Davies, P. J., Simkins, V. R. & Alderson, A. Negative Poisson’s ratio polyester fibers. Text. Res. J. 76, 540–546 (2006).

Simkins, V. R., Ravirala, N., Davies, P. J., Alderson, A. & Alderson, K. L. An experimental study of thermal post-production processing of auxetic polypropylene fibres. Phys. Status Solidi B Basic Res. 245, 598–603 (2008).

Article  ADS  CAS  Google Scholar 

Ge, Z. & Hu, H. Innovative three-dimensional fabric structure with negative Poisson’s ratio for composite reinforcement. Text. Res. J. 83, 543–550 (2013).

Wang, Z., Hu, H. & Xiao, X. Deformation behaviors of three-dimensional auxetic spacer fabrics. Text. Res. J. 84, 1361–1372 (2014).

Chan, N. & Evans, K. E. Fabrication methods for auxetic foams. J. Mater. Sci. 32, 5945–5953 (1997).

Article  ADS  CAS  Google Scholar 

Grima, J. N., Alderson, A. & Evans, K. E. An alternative explanation for the negative poisson’s ratios in auxetic foams. J. Phys. Soc. Jpn. 74, 1341–1342 (2005).

Article  ADS  CAS  Google Scholar 

Jiang, L., Gu, B. & Hu, H. Auxetic composite made with multilayer orthogonal structural reinforcement. Compos. Struct. 135, 23–29 (2016).

Alderson, K. L. et al. How to make auxetic fibre reinforced composites. Phys. Status Solidi Basic Res. 242(3), 509–518 (2005).

Article  ADS  CAS  Google Scholar 

Zhou, L., Jiang, L. & Hu, H. Auxetic composites made of 3D textile structure and polyurethane foam. Phys. Status Solidi Basic Res. 253(7), 1331–1341 (2016).

Article  ADS  CAS  Google Scholar 

Khan, M. I. et al. Development of composites, reinforced by novel 3D woven orthogonal fabrics with enhanced auxeticity. J. Ind. Text. 49(5), 676–690 (2019).

Zulifqar, A. & Hu, H. Development of bi-stretch auxetic woven fabrics based on re-entrant hexagonal geometry. Phys. Status Solidi Basic Res. 256(1), 1800172 (2019).

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Physics Department, Faculty of Science, Galala University, New Galala City, 43511, Egypt

Composite Centre, Advanced Manufacturing Research Centre (AMRC), University of Sheffield, Sheffield, S60 5TZ, UK

Physics Department, Faculty of Science, Mansoura University, Mansoura, 35516, Egypt

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

H.E.-D. have performed the experimental work and completed the manuscript include the results analysis and discussion. C.H. have created the 3D weave design and produced the woven fabric samples used in this work. Both authors reviewed the manuscript.

Correspondence to Hassan M. El-Dessouky.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit

El-Dessouky, H.M., McHugh, C. Multifunctional auxetic and honeycomb composites made of 3D woven carbon fibre preforms. Sci Rep 12, 22593 (2022).


Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Scientific Reports (Sci Rep) ISSN 2045-2322 (online)

Multifunctional auxetic and honeycomb composites made of 3D woven carbon fibre preforms | Scientific Reports

Polyester Spun Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.